XPS depth profile of plasma-activated surface of beech wood (Fagus sylvatica) and its impact on polyvinyl acetate tensile shear bond strength
| Autoři | |
|---|---|
| Rok publikování | 2015 |
| Druh | Článek v odborném periodiku |
| Časopis / Zdroj | WOOD SCIENCE AND TECHNOLOGY |
| Fakulta / Pracoviště MU | |
| Citace | |
| www | http://rdcu.be/mQ7n |
| Doi | https://doi.org/10.1007/s00226-014-0691-7 |
| Obor | Fyzika plazmatu a výboje v plynech |
| Klíčová slova | barrier discharge; atmospheric-pressure; adhesion properties; air; wettability; extractives |
| Popis | High surface selectivity of atmospheric pressure plasma treatment was demonstrated experimentally by XPS depth profile measurement of plasma-activated beech wood. Wood surface activated by diffuse coplanar surface barrier discharge was sequentially sputtered by Ar+ ion beam followed by immediate XPS analysis of freshly uncovered surface. According to the assessment, less than 330 nm of sputtered material was sufficient for complete removal of all plasma-formed functional groups. For the sake of practical implications of minimal vertical extent of plasma-mediated changes, the character of tensile shear bond strength improvement of polyvinyl acetate adhesive was examined with respect to its specific mass. A constant additive character of plasma activation to the bond strength was observed within the examined range of adhesive-specific mass. |